Electrolyte structure for a high-temperature, high-pressure lithium battery

ABSTRACT

A system and a method for forming a composite electrolyte structure are provided. An exemplary composite electrolyte structure includes, at least in part, polymer electrolyte preforms that are bonded into the composite electrolyte structure.

CROSS REFERENCE TO RELATED PATENT APPLICATIONS

This application is a divisional of and claims the benefit of priority to U.S. patent application Ser. No. 16/890,474, filed Jun. 2, 2020. The contents of which are incorporated by reference herein.

TECHNICAL FIELD

This disclosure relates to solid state electrolytes for lithium ion batteries.

BACKGROUND

Downhole logging tools, such as wireline logging tools, measurement while drilling (MWD), and logging while drilling (LWD), are often used to obtain information about the geological formations, hydrocarbons, drilling tools and fluids in and around a wellbore. These tools may be connected to a line from the surface, termed a wireline, that provides both power and data access. The depth of many wells, especially in a subsea environment, may make the use of a wireline impractical. Accordingly, battery-powered devices are in development to allow measurements to be taken in a wellbore.

However, battery-operated devices for downhole equipment often operate in harsh wellbore environments, such as high temperatures (greater than about 200° C.) and high pressures (up to about 20,000 psi). Therefore, new high pressure, high temperature (HPHT) battery technologies are needed for many downhole applications.

SUMMARY

An embodiment described herein provides a method for making an electrolyte for a high-temperature, high-pressure lithium ion battery. The method includes coating polymer electrolyte particles with an oxide to make coated polymer electrolyte particles and printing a polymer electrolyte preform in a binder jet printer from the coated polymer electrolyte particles and a composite electrolyte structure is formed, at least in part from the polymer electrolyte preform.

Another embodiment described herein provides a composite electrolyte structure. The composite electrolyte structure includes, at least in part, polymer electrolyte preforms that are bonded into the composite electrolyte structure.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a schematic drawing of a high temperature high pressure (HTHP) lithium ion battery (LIB) in use.

FIG. 2 is a process flow drawing of a method for the formation of a composite electrolyte structure.

FIG. 3 is a drawing of a coated polymer electrolyte particle.

FIG. 4 is a schematic drawing of the three dimensional printing of an electrolyte preform using a binder jet printing technique.

FIG. 5A is a drawing of a polymer electrolyte preform formed from polymer electrolyte particles having an oxide coating.

FIG. 5B is a drawing of a ceramic electrolyte preform formed from ceramic particles.

FIG. 6A is a schematic drawing of the pulse bonding of a number of polymer electrolyte preforms formed from polymer electrolyte particles into a composite electrolyte structure using spark plasma sintering.

FIG. 6B is a schematic drawing of the bonding of a number of polymer electrolyte preforms formed from polymer electrolyte particles into a composite electrolyte structure using microwave sintering (MWS)

FIG. 6C is a schematic drawing of the composite electrolyte structure formed from the polymer electrolyte preforms after application of an oxide coating by atomic layer deposition.

FIG. 7A is a schematic drawing of the bonding of alternating polymer electrolyte preforms and ceramic electrolyte preforms into a composite electrolyte structure using spark plasma sintering.

FIG. 7B is a schematic drawing of the bonding of alternating polymer electrolyte preforms and ceramic electrolyte preforms into a composite electrolyte structure using microwave sintering (MWS)

FIG. 7C is a schematic drawing of the composite electrolyte structure formed from both polymer electrolyte preforms and ceramic preforms after application of an oxide coating by atomic layer deposition.

DETAILED DESCRIPTION

Reliable rechargeable downhole energy systems with high energy density capable of operating at high temperatures and high pressures, termed HTHP herein, would be useful for both onshore and offshore applications. The downhole temperatures in onshore wellbores typically range from 150° C. to 250° C. For offshore applications, in addition to the high temperatures, high pressures of up to 20,000 psi are often encountered. Currently, the operating temperatures for primary and non-rechargeable batteries, for example, for MWD/LWD applications, range from about 160° C. to about 180° C.

Lithium-ion batteries (LIBs) have gradually become an important power source for many applications, including power leveling, transportation, electronics, and oil-field equipment, among many others. The performance of lithium-ion batteries depends on the materials used, so the development of new materials is important to facilitate the development of battery technology for new applications.

The development of new materials has two focal points. The first is the development of electrode materials that have high-energy, rapid charge and discharge, and long-term stability. The other is the development of different types of electrolytes for different purposes. Expanding the operating temperature range of LIBs is an important consideration. Since the liquid electrolytes used in conventional LIBs are mainly based on LiPF₆ lithium salts, thionyl chloride, and low-boiling organic solvents, such as propylene carbonate (PC) and ethylene carbonate (EC), they cannot operate steadily and safely at higher temperatures than their functional temperature. Accordingly, solid electrolytes that are suitable for high temperature working environments are a research target. The techniques disclosed herein are directed to new electrolyte materials for rechargeable HTHP LIBs for these types of environments.

The use of solid electrolytes eliminates the need for sealed liquid electrolytes, simplifying battery design, improving safety and durability. Solid-state batteries have many advantages, such as the elimination of the risk of spontaneous combustion or explosion. Traditional lithium-ion batteries with electromechanical electrolytes are prone to heat generation in the electrolyte under abnormal conditions, such as overcharging and internal short circuits, and there is a risk of spontaneous combustion or even explosion. All solid lithium batteries are made of solid materials, which are non-flammable, non-corrosive, non-volatile, and have no liquid leakage. Other types of LIBs, such as semi-solid and quasi-solid batteries, still have a certain risk of flammability but the safety is higher than liquid electrolyte batteries.

Further, solid-state batteries do not require electrolytes or diaphragms for electrolyte expansion. These two parts add up to nearly 40% of the volume and 25% mass in conventional LIBs. Thus, the battery housing and cooling system module can be simplified to further reduce the weight of the battery system. In addition, the new positive and negative materials can enable electrochemical windows to reach more than 5V, which can fundamentally increase energy density, estimated to reach 500 Wh/Kg.

FIG. 1 is a schematic drawing of a high temperature high pressure (HTHP) lithium ion battery (LIB) 100 in use. In the HTHP LIB 100, electrons flow from an anode current collector 102, such as a copper film to power a load 104. As the electrons are removed from the anode current collector 102, electrons are formed in the anode material 106, as lithium atoms are converted to Li⁺ ions. The Li⁺ ions are transported from the anode material 106 through an electrolyte layer 108 to a cathode material 112.

After powering the load 104, the electrons are returned to the HTHP LIB 100 through a cathode current collector 110. From the cathode current collector 110, the electrons are transported to a cathode material 112, in which the electrons combine with the Li⁺ ions to form Li⁰ atoms. The Li⁰ atoms are then stored in the cathode material 112.

As described further herein, in the HTHP LIB 100 the electrolyte layer 108 is a composite electrolyte structure. In some embodiments, the composite electrolyte structure includes multiple layers of a solid polymer electrolyte. In other embodiments, the composite electrolyte structure includes multiple layers of both a solid polymer electrolyte and a ceramic electrolyte. In some embodiments, the composite electrolyte structure is formed of alternating layers of a solid polymer electrolyte and a ceramic electrolyte.

FIG. 2 is a process flow drawing of a method 200 for the formation of a composite electrolyte structure. The method 200 begins at block 202 with the coating of polymer electrolyte particles with an oxide. In various embodiments, the polymer electrolyte particles include poly(vinylidene fluoride)-co-hexafluoropropylene (PVDF-HFP), poly(ethylene oxide) (PEO), poly (Methylmethacrylate) (PMMA), polyacrylonitrile (PAN), or other polymers. In various embodiments, the oxide is a nanocoating of a ceramic material, such as Al₂O₃, SiO₂, ZrO₂, Y₂O₃, or a combination thereof.

In some embodiments, the coating is performed by atomic layer deposition (ALD), for example, by flowing reagents through a fluidized powder bed. ALD is a type of chemical vapor deposition in which the material to be coated is sequentially exposed to reactive precursors.

In some embodiments, hydroxyl groups may be formed on the surface of the polymer electrolyte particles by functionalization, plasma treatment, heat treatment, or other techniques. A first precursor is introduced to react with the hydroxyl groups on the surface. In some embodiments in which the coating is Al₂O₃, the first precursor is an organoaluminum, such as trimethyl aluminum (TMA) or triethyl aluminum (TEA), among others. The organoaluminum reacts with the hydroxyl groups until there are no more hydroxyl groups left. The reaction chamber, or fluidized bed, is then purged to remove excess organoaluminum vapor and a second precursor is introduced. In some embodiments, the second precursor is water. The water reacts with the organoaluminum on the surface, forming a layer of aluminum oxide. If a thicker layer is desirable, these steps may be repeated, wherein the last step in each iteration is the reaction with water.

In some embodiments in which the coating is SiO₂, a catalytic ALD process is used. In some embodiments, the first precursor is mixture of silicon tetrachloride (SiCl₄) and a Lewis-based catalyst, such as ammonia, which reacts with hydroxyl groups on the surface to form Si—O bonds. The reaction chamber, or fluidized bed, is then purged remove excess mixture, after which the second precursor is added, such as a water and ammonia mixture. The steps may be repeated to form a thicker layer of SiO₂. The coated polymer electrolyte particle is discussed further with respect to FIG. 3 .

In various embodiments, ceramic electrolyte preforms are made from ceramic particles, such as lithium super-ion conductor solid electrolytes (LISICON), including Li₁₄Zn (GeO₄)₄ and Li_(3.25)Ge_(0.25)P_(0.75)S₄, among others. The ceramic particles may not be coated before use. However, in some embodiments, the ceramic electrolyte particles are coated as described above.

At block 204, electrolyte preforms are made from the coated or uncoated electrolyte particles using 3D printing, for example, in a binder jet printer. In the binder jet printing process a binder oligomer, such as an acrylate oligomer and an initiator, is printed over a powder in a layer to form a pattern. The polymerization of the binder oligomer is initiated by exposure to light or heat and the polymerization fixes the pattern in place. In some embodiments, the parts are heat treated after the preform is made. The 3D printing to form the electrolyte preforms is described further with respect to FIG. 4 . Specific examples of the electrolyte preforms are shown in FIGS. 5A and 5B.

At block 206, the electrolyte preforms are assembled into a composite electrolyte structure and bonded together. In some embodiments, the bonding is performed by spark-plasma sintering (SPS). The specific electrolyte preforms chosen to form the composite electrolyte structure depend on the temperature of use. In embodiments in which the temperature of use is less than about 150° C., polymer electrolyte preforms are bonded together to form the composite electrolyte structure. In embodiments in which the temperature of use is greater than about 200° C., a ceramic electrolyte preform is placed between each of the polymer electrolyte preforms to enhance the temperature resistance in the high-temperature application. In addition to bonding the electrolyte preforms into the composite electrolyte structure, the SPS densifies the solid electrolytes and increases the interconnections. The use of SPS to bond the electrolyte preforms into the composite electrolyte structure is discussed further with respect to FIGS. 6A and 7A.

At block 206, in some embodiments, the bonding is performed by microwave sintering (MWS), as an alternative to spark-plasma sintering (SPS). In addition to bonding the electrolyte preforms into the composite electrolyte structure, the MWS densifies the solid electrolytes and increases the interconnections. The use of MWS to bond the electrolyte preforms into the composite electrolyte structure is discussed further with respect to FIGS. 6B and 7B.

At block 208, the composite electrolyte structure is coated with an oxide for further protection. In some embodiments, this is performed by ALD, for example, using the chemical process described with respect to block 202 to apply a coating of an oxide to the entire bonded structure.

FIG. 3 is a drawing of a coated polymer electrolyte particle 300. In various embodiments, the polymer electrolyte particle 300 is spherical, as shown in FIG. 3 . Although, the polymer electrolyte particle 300 may be any number of other shapes, including random particles. In some embodiments, the polymer electrolyte particle 300 is between about 20 μm and about 1000 μm in diameter, or between about 15 μm and about 60 μm in diameter, or about 40 μm in diameter.

The polymer electrolyte particle 300 has a core 302 that is a polymer electrolyte, for example, as described with respect to FIG. 2 . The coating 304 is an oxide, or ceramic, that protects the polymer electrolyte particle 300. In some embodiments, the coating 304 is between about 1 nm and about 100 nm in thickness, or between about 10 nm and 50 nm in thickness, or about 30 nm in thickness.

FIG. 4 is a schematic drawing 400 of the three dimensional printing of an electrolyte preform 402 using a binder jet printing technique. In the binder jet printing technique, a roller 404 is used to spread a layer of electrolyte particles 406 over a platform 408 in a building chamber (not shown). A printhead 410 is used to print a pattern of a binder solution 412 over the layer of electrolyte particles 406. As used herein, the electrolyte particles 406 are either polymer electrolyte particles or ceramic electrolyte particles. In some embodiments, a mixture of polymer electrolyte particles and ceramic electrolyte particles is used to create the electrolyte preform. In some embodiments, as the printhead 410 creates the pattern, a radiation source 414 is used to initiate polymerization of the binder, such as with a UV light source activating a photoinitiator or an infrared source activating a thermal initiator.

As each layer is printed, the platform 408 is lowered, and a new layer of electrolyte particles 406 is spread over the top of the platform 408 and electrolyte preform 402 by the roller 404. The printhead 410 then prints a new pattern of binder solution 412. In some embodiments, the new pattern is fixed by radiation from the radiation source 414, before the platform 408 is lowered for another layer. Completion of the binder jet printing process results in a formed electrolyte preform 402, which is used to form the composite electrolyte structure.

FIG. 5A is a drawing of a polymer electrolyte preform 502 formed from polymer electrolyte particles having an oxide coating. The polymer electrolyte preform 502 is a green part, for example, including between about 10 vol. % percent and about 40 vol. % binder and air, or between about 20 vol. % and about 30 vol. % binder and air, or about 25 vol. % binder and air. As described herein, in some embodiments, the binder is polymerized during the printing process allowing the direct removal of the polymer electrolyte preform 502 from the loose polymer electrolyte particles. In some embodiments an initiation step is not used during the printing process and the polymer electrolyte preform 502 and loose binder particles are left together during a heating cycle to initiate the polymerization of the binder and drive off liquids, while the loose binder particles provide support to the polymer electrolyte preform 502.

The polymer electrolyte preform 502 is between about 100 μm and about 700 μm in thickness or between about 300 μm and about 500 μm in thickness. In some embodiments, the polymer electrolyte preform is about 400 μm in thickness.

FIG. 5B is a drawing of a ceramic electrolyte preform 504 formed from ceramic particles. The ceramic electrolyte preform 504 is formed from ceramic electrolyte particles using the same binder jet process as for the polymer electrolyte preform 502. As for the polymer electrolyte preform 502, the ceramic electrolyte preform 504 is a green part, for example, including between about 10 vol. % percent and about 40 vol. % binder and air, or between about 20 vol. % and about 30 vol. % binder and air, or about 25 vol. % binder and air. As described herein, in some embodiments, the binder is polymerized during the printing process allowing the direct removal of the ceramic electrolyte preform 504 from the loose ceramic electrolyte particles. In some embodiments an initiation step is not used during the printing process, and the ceramic electrolyte preform and loose binder particles are left together during a heating cycle to initiate the polymerization of the binder and drive off liquids while the loose binder particles provide support to the ceramic electrolyte preform 504.

FIG. 6A is a schematic drawing of the pulse bonding of a number of polymer electrolyte preforms 502 formed from polymer electrolyte particles into a composite electrolyte structure 602 using spark plasma sintering. Like numbered items are as described with respect to FIG. 5 . The SPS is performed by holding the parts together in a die using a clamp, for example, having a conductive graphite surface for the jaw of the clamp. In various embodiments, two, three, five, six, seven, or more, polymer electrolyte preforms 502 may be bonded to form a composite electrolyte structure 602. In various embodiments, the SPS processing parameters include an applied pressure between 50 and 100 MPa, pulse cycles with a period of 2.5 ms and in a pattern of 12 cycles on and 2 cycles off, and a maximum pulse amperage 604 of 10,000 A and DC voltage of 10 V.

The SPS bonding both sinters the individual polymer electrolyte preforms 502 together to form the final composite electrolyte structure 602 and densifies the polymer electrolyte preforms 502. The densification of the polymer electrolyte preforms 502 burns away binder, and decreases the empty airspace between the coated polymer electrolyte particles.

The bonding is not limited to SPS. In some embodiments, the bonding of the polymer electrolyte preforms 502 is performed by microwave sintering (MWS).

FIG. 6B is a schematic drawing of the bonding of a number of polymer electrolyte preforms 502 formed from polymer electrolyte particles into a composite electrolyte structure 602 using microwave sintering (MWS). The polymer electrolyte preforms 502 are placed in the microwave sintering chamber 606. Microwave energy is injected into the chamber through a microwave port 608. The heat is applied by triggering the interaction of the preforms and the electromagnetic energy in the frequency range of 300 MHz to 300 GHz. The localized heat among the particles in the preforms sinters them into the densified part.

FIG. 6C is a schematic drawing of the composite electrolyte structure 602 formed from the polymer electrolyte preforms 502 after application of an oxide coating 610 by atomic layer deposition. As described with respect to FIG. 2 , the oxide coating may be applied by sequentially reacting precursors with chemical moieties, such as hydroxyl groups, on the surface.

In various embodiments, the composite electrolyte structure 602 formed from the polymer electrolyte preforms 502 is used up to a temperature of about 150° C. However, in many applications in downhole environments, the temperature will be higher than this. Accordingly, in embodiments described herein, the use of ceramic electrolyte preforms 504 (FIG. 5B), such as in an alternating configuration with the polymer electrolyte preforms 502, is used to increase the thermal stability of a composite electrolyte structure.

FIG. 7A is a schematic drawing of the bonding of alternating polymer electrolyte preforms 502 and ceramic electrolyte preforms 504 into a composite electrolyte structure 702 using spark plasma sintering. Like numbered items are as described with respect to FIGS. 5 and 6 . As described herein, ceramic electrolytes have high stability over a wide temperature range, especially at high temperatures of greater than about 200° C., providing batteries that may be useful up to about 550° C. However, these electrolytes have a number of issues, including volume changes in electrode materials, large interface (electrode/electrolyte) resistance, low quality of electrode active materials, and poor cycle stability.

One of the most important issues that needs to be overcome for ceramic electrolyte is improvements in the ion conductivity of the electrode interface. During battery cycles (charge and discharge), active electrodes often experience structural fragmentation, resulting in capacity decay. Solid electrolytes with low elastic modulus are always preferred because this reduces the degree of fragmentation of the electrode material. In LiPON solid electrolytes, for example, lithium-ion transport is often hampered by the interface, while LiPON's high elastic modulus and hardness are resistant to lithium dendrites.

For battery assembly, fabrication, and manufacturing, interface contact between active electrodes and solid electrolytes can be an extremely important factor in the overall performance of the battery. In general, the malleability and ductility of solid electrolytes and electrodes have significant effects on the contact conditions of the electrode/electrolyte interface. Accordingly, the more flexible polymer electrolyte preforms may reduce fragmentation and increase contact with the electrode.

Further, coating of the particles or composite electrolyte structure with an oxide or other ceramic, such as TiN, Al₂O₃, ZnO, ZrO₂, CeO₂, or Al doped ZnO, may improve the conductivity and circulation stability. The coating ALD formed Al₂O₃ film may improve the wetting of the interface. Similarly, ultra-thin LiPON film can be evenly applied to the surface of the particles through ALD, thereby reducing the interface contact resistance.

In various embodiments, the composite electrolyte structure 702 may include alternating layers of polymer electrolyte preforms 502 and ceramic electrolyte preforms 504 with a total number of electrolyte preforms 502 and 504 of two, three, four, five, six, seven, or more. In some embodiments, the polymer electrolyte preforms 502 form the outer layers of the composite electrolyte structure 702 to enhance the connectivity to electrodes. In these embodiments, an odd number of electrolyte preforms 502 and 504 may be included, such as three, five, seven, or more.

The bonding of the electrolyte preforms 502 and 504 is not limited to spark plasma sintering. In some embodiments, the bonding among the polymer electrolyte preforms and ceramic electrolyte preforms into a hybrid electrolyte structure is performed by microwave sintering (MWS) as schematically shown in FIG. 7B.

FIG. 7B is a schematic drawing of the bonding of alternating polymer electrolyte preforms 502 and ceramic electrolyte preforms 504 into a composite electrolyte structure 702 using microwave sintering (MWS). The stack of alternating electrolyte preforms 502 and 504 are placed in the microwave sintering chamber 606. Microwave energy is injected into the chamber through a microwave port 608. The heat is applied by triggering the interaction of the preforms and the electromagnetic energy in the frequency range of 300 MHz to 300 GHz. The localized heat among the particles in the preforms sinters them into the densified part.

FIG. 7C is a schematic drawing of the composite electrolyte structure 702 formed from both polymer electrolyte preforms 502 and ceramic preforms 504 after application of an oxide coating 610 by atomic layer deposition. As described herein, the coating process may be performed by sequential reaction of surface functional groups with precursor chemicals, as described herein. In various embodiments, the composite electrolyte structure 702 formed from the combination of the polymer electrolyte preforms 502 and the ceramic electrolyte preforms 504 is used in applications in which the temperature is greater than about 200° C.

An embodiment described herein provides a method for making an electrolyte for a high-temperature, high-pressure lithium ion battery. The method includes, coating polymer electrolyte particles with an oxide to make coated polymer electrolyte particles and printing a polymer electrolyte preform in a binder jet printer from the coated polymer electrolyte particles and a composite electrolyte structure is formed, at least in part from the polymer electrolyte preform.

In an aspect, the oxide on the polymer electrolyte particles is applied by atomic layer deposition. In an aspect, a number of polymer electrolyte preforms are bonded into the composite electrolyte structure by spark plasma sintering. In an aspect, a number of polymer electrolyte preforms are bonded into the composite electrolyte structure by microwave sintering.

In an aspect, the composite electrolyte structure is coated with the oxide. In an aspect, the oxide is supplied to the composite electrolyte structure by atomic layer deposition.

In an aspect, a ceramic electrolyte preform is printed in the binder jet printer from ceramic electrolyte particles. In an aspect, the composite electrolyte structure is formed by bonding alternating polymer electrolyte preforms and ceramic electrolyte preforms. In an aspect, the composite electrolyte structure is coated with the oxide. In an aspect, the oxide is supplied to the composite electrolyte structure by atomic layer deposition.

Another embodiment described herein provides a composite electrolyte structure. The composite electrolyte structure includes, at least in part, polymer electrolyte preforms that are bonded into the composite electrolyte structure.

In an aspect, the polymer electrolyte preforms include polymer electrolyte particles coated with an oxide. In an aspect, the polymer electrolyte particles comprise poly(vinylidene fluoride)-co-hexafluoropropylene (PVDF-HFP), or poly(ethyleneoxide) (PEO), poly (methylmethacrylate) (PMMA), polyacrylonitrile (PAN), or any combinations thereof. In an aspect, the oxide comprises Al₂O₃, SiO₂, ZrO₂, Y₂O₃, or any combinations thereof.

In an aspect, the polymer electrolyte preforms comprise a binder from a binder jet printer. In an aspect, the binder is removed during a bonding process by spark plasma sintering or microwave sintering. In an aspect, the composite electrolyte structure includes an oxide applied over the composite electrolyte structure.

In an aspect, the composite electrolyte structure includes ceramic electrolyte preforms that are bonded into the composite electrolyte structure with the polymer electrolyte preforms. In an aspect, the ceramic electrolyte preforms alternate with polymer electrolyte preforms. In an aspect, the ceramic electrolyte preforms comprise a binder from a binder jet printer. In an aspect, the binder is removed during a bonding process by spark plasma sintering or microwave sintering. In an aspect, the composite electrolyte structure includes an oxide coating applied over the composite electrolyte structure.

Other implementations are also within the scope of the following claims. 

1-10. (canceled)
 11. A composite electrolyte structure, comprising at least, in part, polymer electrolyte preforms that are bonded into the composite electrolyte structure.
 12. The composite electrolyte structure of claim 11, wherein the polymer electrolyte preforms comprise polymer electrolyte particles coated with an oxide.
 13. The composite electrolyte structure of claim 12, wherein the polymer electrolyte particles comprise poly(vinylidene fluoride)-co-hexafluoropropylene (PVDF-HFP), or poly(ethyleneoxide) (PEO), poly (methylmethacrylate) (PMMA), polyacrylonitrile (PAN), or any combinations thereof.
 14. The composite electrolyte structure of claim 12, wherein the oxide comprises Al₂O₃, SiO₂, ZrO₂, Y₂O₃, or any combinations thereof.
 15. The composite electrolyte structure of claim 11, wherein the polymer electrolyte preforms comprise a binder from a binder jet printer.
 16. The composite electrolyte structure of claim 15, wherein the binder is removed during a bonding process by spark plasma sintering.
 17. The composite electrolyte structure of claim 11, comprising an oxide applied over the composite electrolyte structure.
 18. The composite electrolyte structure of claim 11, comprising ceramic electrolyte preforms that are bonded into the composite electrolyte structure with the polymer electrolyte preforms.
 19. The composite electrolyte structure of claim 18, wherein the ceramic electrolyte preforms alternate with polymer electrolyte preforms.
 20. The composite electrolyte structure of claim 18, wherein the ceramic electrolyte preforms comprise a binder from a binder jet printer.
 21. The composite electrolyte structure of claim 20, wherein the binder is removed during a bonding process by spark plasma sintering or microwave sintering.
 22. The composite electrolyte structure of claim 18, comprising an oxide coating applied over the composite electrolyte structure.
 23. The composite electrolyte structure of claim 17, wherein the oxide is applied over the composite electrolyte structure by atomic layer deposition.
 24. The composite electrolyte structure of claim 17, wherein the oxide is applied over the composite electrolyte structure by atomic layer deposition.
 25. The composite electrolyte structure of claim 15, wherein the binder is removed during a bonding process by microwave sintering. 